牌号简介 About |
---|
Lexan 3412ecr树脂Lexan 3412ecr聚碳酸酯(PC)树脂是一种20%玻璃纤维填充,注塑成型等级。这种无氯、无溴阻燃剂GF-PC具有UL-94V0等级,可用于各种不透明颜色选择。Lexan 3412ECR是一种专为满足高刚度应用需求而设计的树脂。 LEXAN 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in various opaque color options. LEXAN 3412ECR is a resin designed to meet the needs of high stiffness applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ASTM D792 |
密度 Density |
1.36 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
7.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
7.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.20 to 0.50 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/5 | |
屈服 yield |
% | ISO 527-2/5 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 9 |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance 11 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
11 钨电极 |
【新闻资讯】查看全部
从废塑料瓶到冷链保温材料 亨斯迈聚氨酯产品实现重大突破
2020-12-19 搜料网资讯:近日,亨斯迈集团发布了升级版四大可持续创新解决方案,实现了从1.0到2.0的转变。升级后的四大可持续创新解决方案与之前的方案相比,更加贴近终端市场客户的需求。 |
从废塑料瓶到冷链保温材料 亨斯迈聚氨酯产品实现重大突破 搜料网资讯:近日,亨斯迈集团发布了升级版四大可持续创新解决方案,实现了从1.0到2.0的转变。升级后的四大可持续创新解决方案与之前的方案相比,更加贴近终端市场客户的需求。今年因为疫情的发展,让亨斯迈注意到冷链市场对优质解决方案的迫切需求,将食物供应链解决方案作为新的重要发力点。 “如果缺少冷链,全球的食物将近三分之一被浪费。在过去的中国乃至现在的中国,因为缺少冷链,蔬菜水果可能达到40%的损害。一方面来自市场本身切实的需要;另一方面,疫情给冷链物流行业带来了增长的契机,基于这两点,冷链市场的发展空间非常大。”亨斯迈聚氨酯事业部商务总监/中国区总经理张骏表示。 此次,亨斯迈瞄准蓬勃增长的现代农业和物流冷链中的仓储环节,通过提供绿色安全的保温材料,旨在助力中国解决当前突出的食品安全问题,并推动更快的业务增长。 聚氨酯是目前为止市场上保温性能最好的一种材料,跟其他的保温材料相比,至少可以节约20%的能源,因此被广泛用于建筑保温行业。过去的聚氨酯保温材料,在建筑保温应用中,最大的挑战来自于他的防火性能,保温与防火往往无法兼顾。亨斯迈Terol™泰络优™聚酯多元醇产品的出现打破了这一局面,可以同时实现保温和阻燃。 亨斯迈Terol™泰络优™聚酯多元醇是使用回收的塑料瓶生产的产品,其成分中高达60%来自回收PET塑料。“它的化学结构非常稳定,防火性能相比现在普遍使用的其他类似相关材料有很大的提升,所以我们把这个产品作为一个新的商机,希望能够用我们先进的材料和解决方案,提升聚氨酯建筑保温行业产品水准,推动整个冷链物流产业的升级。”张骏告诉记者。 12月1日,亨斯迈集团与河南超诚建材科技有限公司在新乡举办首批基于泰络优™聚酯多元醇的聚氨酯连续板材下线仪式,实现了从产品原材料到成品的落地。随着泰络优™聚酯多元醇产品台湾工厂在今年5月份的投产、亨斯迈聚氨酯天津组合料工厂在今年6月份产能的释放以及首批基于泰络优™聚酯多元醇的聚氨酯连续板材的下线,亨斯迈正在中国逐步推进和完成以Terol™泰络优™聚酯多元醇产品为价值核心的产业布局。
据了解,亨斯迈现在已经利用泰络优™聚酯多元醇开发出符合B1防火性能的聚氨酯板材,而且已经开始应用于一些国家重大的冷链项目,产品开始走向商业化。 “目前,四大可持续解决方案已经不仅仅是亨斯迈聚氨酯或亨斯迈在亚洲的发展战略,更已经成为亨斯迈在全球未来发展的主要核心理念,只是现在四大可持续解决方案恰巧更多的配合我们在亚洲尤其在中国市场的需求。”亨斯迈聚氨酯亚太区总裁潘律民表示。 其中,塑料垃圾是亨斯迈在实现可持续发展目标过程中面临的一个很重大的课题,亨斯迈希望能在实现可持续发展的同时,也能够做到价值创造。“我们这么多年来,在践行可持续发展过程中所学习到的最重要的一点,就是我们要能够把可持续发展和价值创造结合在一起。”潘律民说。 Terol™泰络优™聚酯多元醇是一个很好的佐证,Terol™泰络优™聚酯多元醇下游应用包括现代农业、冷链仓储、以及管道保温等,创造了价值的同时也兼顾了可持续发展。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。