牌号简介 About |
---|
XHT2146树脂是一种高流动性、高热聚碳酸酯共聚物,与Lexan XHT2141树脂相比,其释放性能得到了改善。它有一系列不透明和有限透明的颜色。 XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to LEXAN XHT2141 resin. It is available in a range of opaque and limited transparent colors. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:Automotive Lighting;
加工条件:注射成型 Injection Molding
性能特点: 含脱模剂; 共聚物; 耐高温; 流动性高; High liquidity,Good stripping performance,High Heat Resistance,Copolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
330℃,2.16kg 330℃,2.16kg |
46 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
330℃,2.16 kg 330℃,2.16 kg |
43.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.60 到 0.90 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.30 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 5 , 6 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 8 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 9 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 10 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40℃ TD:-40℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
2. 5.0 mm/min |
3. 类型 1, 50 mm/min |
4. 1.3 mm/min |
5. 2.0 mm/min |
6. at Yield |
7. 80*10*3 sp=62mm |
8. 80*10*3 mm |
9. 80*10*4 mm |
10. 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
海南省抽查不合格产品检出率30.8%
2018-12-13 2018年12月10日,海南省市场监督管理局公布2018年薄膜产品质量省级监督抽查结果,检出4个样品不合格,不合格产品检出率30.8%。 据通报,2018 |
海南省抽查不合格产品检出率30.8% 2018年12月10日,海南省市场监督管理局公布2018年薄膜产品质量省级监督抽查结果,检出4个样品不合格,不合格产品检出率30.8%。 据通报,2018年5月7日至7月6日,原海南省质量技术监督局组织对全省薄膜产品进行了省级监督抽查。本次省级监督抽查涉及12家生产企业13个样品,检出4个样品不合格,不合格产品检出率30.8%。本次抽查包括跟踪上年度不合格企业5家5个批次,经检验2个批次合格,3个批次不合格,连续两年不合格企业为:海口龙华龙泉琼新塑料厂、海南锦云化工塑料有限公司、海南天人降解塑料股份有限公司。 本次抽查检验依据: 1.《2018年海南省薄膜产品质量省级监督抽查方案》; 2.GB/T 21661-2008 塑料购物袋; 3.GB/T 8946-2013 塑料编织袋通用技术要求; 4.GB/T 24454-2009 塑料垃圾袋; 5.GB/T 13519-2016 包装用聚乙烯热收缩薄膜; 6.GB/T 9774-2010 水泥包装袋; 7.YC/T 266-2008 烟用包装膜。 本次抽查检验项目: 1. 塑料购物袋:尺寸偏差、异嗅、外观、提吊试验、跌落试验、漏水性、封合强度、落镖冲击。 2.塑料编织袋:外观质量、允许偏差、拉伸负荷、耐热性能、跌落性能。 3.塑料垃圾袋:尺寸偏差、异嗅、外观、抗渗漏性能、跌落性能。 4.水泥包装袋:外观、单位面积质量、拉伸负荷、适用温度、牢固度、制袋材料对水泥强度的影响、防潮性能、标志。 5.包装用聚乙烯热收缩膜:拉伸强度、断裂标称应变、直角撕裂强度、收缩率。 6.烟用包装膜:拉伸强度、断裂伸长率、热收缩率、雾度、光泽度、热封强度、透湿量、动摩擦系数。 来源:中国质量新闻网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】